What is 5052 aluminum used for?
5052 aluminum is frequently used for general sheet metal work, heat exchangers, flooring panels, rivets and wires, chemical drums and other equipment, pressure vessels, treadplate, containers, and more.
Can you harden 5052 aluminum?
Aluminum 5052 (UNS A95052) in Coil Form It also has the low density and excellent thermal conductivity similar to other aluminum alloys. Alloy 5052 can be hardened by cold work and is not heat treatable to higher strength.
What is aluminum 5052 H32?
Aluminium alloy 5052 in H32 temper has very good corrosion resistance to seawater and marine and industrial atmosphere. It also has very good weldability and good cold formability. It is a medium to high strength alloy with a strength slightly higher than 5251 and a medium to high fatigue strength.
What does aluminum 5052 weigh?
Aluminum Plate – Series 5052-H32
| Item # | Thickness | Sheet Weight per Unit Area |
|---|---|---|
| 5052-H32-375-48-144 | 0.375 inches9.5250 mm | 5.238 lbs/ft²25.571916 kg/m² |
| 5052-H32-500-48-144 | 0.500 inches12.7 mm | 6.984 lbs/ft²34.095888 kg/m² |
| 5052-H32-750-48-144 | 0.750 inches19.05 mm | 10.476 lbs/ft²51.143832 kg/m² |
Can you weld 5052 aluminum?
The correct filler metal for the 5XXX alloys is one of the 5XXX fillers, such as 5356, 5554, 5183, or 5556. However, 5052 is the only 5XXX alloy that cannot be welded autogenously. So you can’t weld 5052 autogenously.
What is the difference between 5005 and 5052 aluminum?
Many people substitute 5052 for 5005. While 5052 can produce acceptable results, it has more imperfections and is more prone to color variation than 5005 alloy aluminum. Talk to your anodizer about your applications, and your expectations for the finish.
What is the density of 5052 aluminum?
2.68 g/cm³
Properties
| Physical Property | Value |
|---|---|
| Density | 2.68 g/cm³ |
| Melting Point | 605 °C |
| Thermal Expansion | 23.7 x10^-6 /K |
| Modulus of Elasticity | 70 GPa |
What is hardness designation for H32?
H28. Strain-hardened and partially annealed – 4/4 hard (fully hardened). H32. Strain-hardened and stabilized – 1/4 hard. H34.
What is 5052 aluminum sheet?
US ASTM AISI and SAE Standards 5052 Aluminum, Alloy 5052H32 H34 Aluminum Sheet and Tube 5052 aluminum is an Al-Mg series aluminum alloy with medium strength, high fatigue strength and good plasticity, and is the most widely used anti-rust material.
What is the difference between 5052 and 3003 aluminum alloy?
Generally, 5052 aluminum alloy is stronger than other popular alloys such as 3003 aluminum and also has improved corrosion resistance due to the absence of copper in its composition. The properties of 5052 aluminum alloy differ based on how it is cold worked, or made stronger using the work-hardening process.
What are the properties of marine grade aluminum 5052 H32?
Notes: The melting temperature range shown applies to wrought products with a thickness of 63.5 mm (1/4 inch) or greater. Marine grade aluminum 5052 H32 mechanical properties are listed in the following tables including yield strength (yield stress), ultimate tensile strength, shear strength, modulus of elasticity, young’s modulus, etc.
What is 5052 steel used for in machining?
It has very good corrosion resistance, and can be easily welded as well. 5052 is not a good choice for extensive machining operations, as it has only a fair machinability rating. It is typically used in aircraft fuel and oil lines, fuel tanks, sheet metal work, appliances, lighting, wire, and rivets.